AWS A 5.17 EH14 Submerged Arc Welding Wire / 25KG-300KG Subarc Wire

Brand Name : CHENXIANG

Model Number : WES EH14

Place of Origin : Shandong, China

MOQ : 1000 kilograms

Packaging Details : 25kg~300kg fine round package; 200kg and 250kg large iron or wood plate package; 25kg/pallet basket package.

Warranty : 3 years

Customized Support : ODM, OBM, OEM

Material : Low Carbon Steel

Diameter : 2.5mm/3.2mm/4.0mm/5.0mm

Melting Point : As Standard

Weight : 25KG-1000KG

Sample : For Free

Delivery : 5-10 days

C : 0.07

Mn : 1.61

Si : 0.03

P : 0.12

S : 0.011

Ni : 0.008

Cr : 0.012

Contact Now

AWS A 5.17 EH14 Submerged Arc Welding Wire / 25KG-300KG Subarc Wire


Product Description


1. Chemical composition
Carbon (C): The content is generally between 0.08% and 0.13%. The appropriate carbon content helps to ensure the strength of the weld metal.


Manganese (Mn): The content is between 1.50% and 1.90%. Manganese can deoxidize and improve the strength and toughness of the weld metal.


Silicon (Si): ≤0.07%. Silicon can improve the strength of the weld to a certain extent, but too high a content may affect the toughness of the weld.


Sulfur (S): ≤0.035%. Sulfur is a harmful element that will reduce the toughness and crack resistance of the weld metal, so its content needs to be strictly controlled.


Phosphorus (P): ≤0.035%. Phosphorus will also reduce the toughness of the weld metal and increase cold brittleness. Its content should also be limited.


2. Performance characteristics

Mechanical properties: The weld metal has a good combination of strength and toughness. Its tensile strength can generally reach 420-560MPa, yield strength is about 330MPa, and elongation is ≥22%, which can meet the use requirements of most engineering structures.


Welding process performance: stable arc combustion, beautiful weld formation, easy slag removal. During the welding process, there is less spatter, which can ensure welding quality and work efficiency.


Details Images


Standard/Grade
GB/T 5293-H10Mn2 AWS EH14
Diameter
2.5mm/3.2mm/4.0mm/5.0mm
Weight
25/50/100/200/250/500/1000KG


AWS A 5.17 EH14 Submerged Arc Welding Wire / 25KG-300KG Subarc Wire


Specifications


One Example of Chemical Composition
Guarantee Value
C
Mn
Si
P
S
Ni
Cr
Cu
Measured Value
Product Tags:

eh14 submerged arc welding wire

      

300kg subarc wire

      

eh14 subarc wire

      
 AWS A 5.17 EH14 Submerged Arc Welding Wire / 25KG-300KG Subarc Wire Manufactures

AWS A 5.17 EH14 Submerged Arc Welding Wire / 25KG-300KG Subarc Wire Images

Inquiry Cart 0
Send your message to this supplier
 
*From:
*To: Hainan Chenxiang New Material Technology Co., Ltd.
*Subject:
*Message:
Characters Remaining: (0/3000)